KUAT TEKAN BETON DENGAN SUBSTITUSI PARSIAL SISA BUBUT BESI SEBAGAI AGREGAT HALUS

##plugins.themes.academic_pro.article.main##

Anggara Yunanda
Rafki Imani
Rita Nasmirayanti

Abstract

One of the concrete technologies developed to obtain good compressive strength of concrete is additional material for iron lathe waste obtained from the residue of the iron turning process. This study aims to determine the effect of iron lathe waste as a fine aggregate additive on the compressive strength of concrete. The compressive strength test of concrete was carried out based on The SNI standard 1974:2011. The sample making of the specimens was carried out by varying 0%, 1.5% and 2.5% of iron lathe waste from the weight of fine aggregate in a concrete mixture with a concrete compressive strength of 29.05 MPa. Concrete samples were tested at the age of 7 days, 14 days, and 21 days. The test results show that the maximum compressive strength of concrete is achieved by normal concrete (0%) which is 28.96 MPa at the age of 21 days of concrete. While the value of the compressive strength of concrete after being given a mixture of iron lathe waste decreased. The optimum concrete compressive strength with the addition of iron lathe waste was obtained at 24.63 MPa with a mixture of 1.5% at the age of 21 days of concrete. The decrease in the compressive strength of concrete due to the addition of iron lathe waste. It occurs because of the air trapped in the concrete, causing the concrete to be hollow and not solid, so that the compressive strength of the concrete decreases.


Keywords: Fine aggregate, Strength of concrete, Waste iron, Concrete technology.

##plugins.themes.academic_pro.article.details##

References

  1. S. Arief and E. Mungok, Chrisna Djaya Samsurizal, “Studi Eksperimen Kuat Tekan Beton Menggunakan Semen Ppc Dengan Tambahan Sikament Ln,” J. PWK, laut, Sipil, Tambang, vol. 2, no. 2, pp. 1–11, 2014.
  2. F. Adibroto, E. Suhelmidawati, and A. A. M. Zade, “Eksperimen Beton Mutu Tinggi Berbahan Fly Ash Sebagai Pengganti Sebagian Semen,” J. Ilm. Rekayasa Sipil, vol. 15, no. 1, pp. 11–16, 2018.
  3. B. A. Fau and A. A. Setiawan, “Studi Eksperimental Kombinasi Gelas dan Tempurung Kelapa Sebagai Substitusi Parsial Agregat Kasar Terhadap Kuat Tekan Beton,” Din. Rekayasa, vol. 15, no. 2, p. 135, 2019.
  4. P. Setiawan, D. S. Adhy, and M. R. Ahyar, “Karakteristik Kuat Tekan Campuran Beton dengan tambahan Serat Tembaga dan Serbuk Besi,” Pondasi, vol. 26, no. 2, p. 72, 2021.
  5. S. Melinda, F. Teknik, J. Sipil, U. Sam, and R. Manado, “Studi Eksperimental Pengujian Kuat Tekan Beton Menggunakan Kapur Dan Batu Apung Sebagai Bahan Pengganti Sebagian Semen,” J. Sipil Statik, vol. 8, no. 5, pp. 671–678, 2020.
  6. P. Riyanto, A. Rahmawati, and A. Nurhidayati, “Studi Eksperimen Kuat Lentur Beton Ramah Lingkungan Berbahan Tambah Abu Ampas Tebu Dan Serat Bambu,” pp. 487–492, 2017.
  7. P. T. Hardagung, Harnung, A Sambowo, dan Gunawan, “Kajian Nilai Slump, Kuat Tekan dan Modulus Elastisitas Beton,” Matriks Tek. Sipil, vol. 2, no. 2, pp. 131–137, 2014.
  8. Y. Kristiandono, and Suharyatma, “Analisis Pengaruh Pencampuran Serat Karbon Terhadap Kekuatan Beton Dalam Menahan Beban Desak,Beban Tarik dan Beban Lentur,” Teknik Sipil UII, Skripsi, 2018.
  9. P. N. Hadi and A. A. Setiawan, “Studi Eksperimental Penambahan Limbah Bubut Sebagai Bahan Subtitusi Parsial Agregat Halus Terhadap Kuat Tekan Beton,” Widyakala J., vol. 6, no. 1, p. 77, 2019.
  10. I. Hanggara, “Pemanfaatan Limbah Bubut Besi pada Beton Serat Ditinjau dari Kuat Tekan Dan Kuat Lentur,” PROKONS Jur. Tek. Sipil, Vol. 13, No. 2, p. 93, 2020.
  11. Standar Nasional Indonesia, SNI-1974:2011Tentang Cara Uji Kuat Tekan Beton.
  12. H. D. Kuntari, A. A. Lingga, and A. Supriyadi, “Analisis Perbandingan Desain Campuran Beton Normal Menggunakan SNI 03-2834-2000 dan SNI 7656 : 2012 dengan Kuat Tekan 30 MPa,” J. Elektron. Laut, Sipil, Tambang, vol. 6, no. 3, 2019.
  13. F. Supriani and M. Islam, “Pengaruh Metode Perlakuan Dalam Perawatan Beton Terhadap Kuat Tekan Dan Durabilitas Beton,” Inersia, J. Tek. Sipil, vol. 9, no. 2, pp. 47–54, 2019.
  14. Kementerian PUPR. 2017. Rancangan Campuran Beton. Diklat Perkerasan Kaku, “Rancangan Campuran Beton,” Diklat Perkerasan Kaku, p. 60, 2017.
  15. SNI 03-2834-2000 Tentang Prosedur Pembuatan Beton Normal.